RT EP 500 2K Epoxy Mica Protective Coating – Matt Finish

Premium Anti-Corrosion Coating for Steel, Bridges, Machinery & Metal Structures

The RT 2K Epoxy Mica Protective Coating is a high-performance epoxy resin coating reinforced with micaceous iron oxide, delivering superior corrosion resistance, abrasion durability, and UV protection. Designed for bridges, railings, docks, pipelines, and metal structures, this matt finish coating ensures long-term protection in aggressive environments, including exposure to seawater, sewage, and harsh chemicals.

🔹 Available for Brush, Roller & Spray Application – Ideal for Industrial & Structural Use.

🔥 Key Features:

✅ Matt Finish – Provides a professional, non-reflective industrial-grade appearance.

✅ Exceptional Corrosion Protection – Formulated with micaceous iron oxide to prevent rust.

✅ High Chemical & Solvent Resistance – Withstands fuels, oils, and industrial cleaning agents.

✅ Heavy-Duty Scratch & Impact Resistance – Ideal for harsh environments.

✅ Excellent UV & Weather Resistance – Maintains durability in extreme conditions.

✅ Direct-to-Metal (DTM) Compatible – Strong adhesion to steel, aluminium, and zinc-coated surfaces.

✅ Electrostatic Application Possible – Suitable for industrial spray systems.

🛠 Best For:

✔ Bridges, railings, and structural steel

✔ Industrial equipment & metal framework

✔ Pipelines, docks & marine environments

🔧 Mixing & Application:

✔ Mixing Ratio: 5:1 by weight | 3:1 by volume with 2K Epoxy Hardener

✔ Thinner: RT Epoxy Thinner

✔ Dilution: Spray Gun: 10 - 15% | Airmix/Airless: 10 - 15% | Brush & Roller: 5 - 10%

✔ Application:

• Gravity Spray Gun: 1.8 - 2.0mm nozzle, 2.0 - 2.5 bar pressure
• Airmix/Airless: 0.33 - 0.54mm nozzle, 100 - 120 bar pressure
• Brush & Roller: Apply in even coats for maximum coverage

⏳ Drying Times:

✔ Dust Dry: 45 - 55 min at 20°C

✔ Set to Touch: 4 - 5 hours at 20°C

✔ Ready for Assembly: 10 - 12 hours at 20°C

✔ Recoatable: 1 hour at 20°C#

💡 For Professional Use Only. Ensure surfaces are properly prepared before application.